The PCBs contribute to the functioning of electronic devices. Thus, they need to be protected from oxidation and damage. The PCB plating is a metal deposition process that assures the protection of these PCBs from oxidation and deterioration. In addition, PCB plating provides clear surface finishing and provides an accurate soldering surface for assembling components. There are different types of plating methods for PCB manufacturing. Are you intrigued to know what they are? If yes, then this post introduces you to the same and also helps you in understanding why plating the printed circuit boards is important.

Goto JYN to know more.

Purpose of Plating PCB

Plating a printed circuit board is beneficial for the following reasons.

• The plating helps improve the aesthetic appeal of the PCB.

• It protects the board from oxidation, moisture, and contamination.

• The PCB plating helps in reducing the overall cost of printed circuit boards and minimizes downtime.

• The plating produces clean and attractive soldering.

PCB Plating Process Discussed in Brief

The PCB plating process proceeds in the following way.

• The first step is the electroless process through which a thin copper layer is deposited on the surface area of the board, as well as the interior of drilled holes. The holes already drilled onto the board are cleaned for residues and contaminants generated during the drilling.

• The interior portion of the hole is prepared with a micro etching, which helps improve the copper binding.

• The photoresist material is added to the bottom and top of the board and exposed to UV light. This UV exposure is limited to free areas which have no patterns.

• Next, the photoresist is washed off, and the board areas are masked by the photoresist, which is hardened.

• The board is connected to the cathode of an electrical current and immersed for plating in a chemical bath.

• Dissolved copper is drawn to the negative charge and deposited on the exposed circuitry.

• The board is next dipped into the cleaning and plating baths to produce an even copper layer.

• After this, the tin is plated on the copper to protect the circuitry.

• Next, non-circuitry copper and photoresist are removed.

• Tin is removed in the final step, and the copper circuitry remains.

4 Types of PCB Plating Methods for PCB Manufacturing

There are four main types of PCB plating methods, and they are described as below:

• Through-Hole Plating:

  Through-hole plating is mainly used for the drilling process. This method uses electroless copper plating, which makes the inner walls of holes conducive to connecting the printed circuit boards easily.

• Brush Plating/Selective Plating:

  This is a portable method of electroplating the printed circuit boards. This plating method is widely used for applying electro-plated deposits and anodized coating on the printed circuit boards. No immersion tanks are used in this process.

• Finger-plated Plating:

  Finger-plating technique is often known as protruding partial plating, where rare metals are plated on the edge connectors, gold fingers, or edge joints of the board. The rare metals help improve the abrasive resistance and minimize contact resistance of the board.

• Reel Linkage Selective Plating:

  Reel linkage selective plating is a reel to reel plating method, allowing selective deposition of metals on components such as transistors, integrated circuits, and connectors.

Understanding these types of plating methods for PCB manufacturing will help you make informed decisions. However, that is not enough. To take advantage of these methods, you need to partner with trusted manufacturers like Creative Hi-Tech. Located in Illinois, the company has been delivering PCBs to its clients in aerospace and satellite, medical, military, wireless, and other industries for several years now. Thus, it perfectly understands the operating environments of PCBs and their plating requirements. The experts at the company will guide you through the suitable plating material and offer you benefits of the same.

Related Blog Posts:

Printed Circuit Board Surface Finishes: Advantages and Disadvantages

By Al Wright, PCB Field Applications Engineer
Epec Engineered Technologies

Anyone involved within the printed circuit board (PCB) industry understand that PCBs have copper finishes on their surface. If they are left unprotected then the copper will oxidize and deteriorate, making the circuit board unusable. The surface finish forms a critical interface between the component and the PCB. The finish has two essential functions, to protect the exposed copper circuitry and to provide a solderable surface when assembling (soldering) the components to the printed circuit board.

Hot Air Solder Leveling (HASL) was once the tried and true method of deliver consistent assembly results. However, the ever-increasing circuit complexity and component density has stretched the capabilities of even horizontal solder levelling systems to their limits.

As component pitches became finer and a need for a thin coating became greater, HASL represented a process limitation for PCB manufacturers. As an alternative to HASL, alternative coatings have been around for several years now, both electrolytic and immersion processes.

Here are a few PCB surface finish options. Listed below are some more common surface finishes used in PCB manufacturing.

Want more information on PCB Plating Line? Feel free to contact us.

HASL / Lead Free HASL

HASL is the predominant surface finish used in the industry. The process consists of immersing circuit boards in a molten pot of a tin/lead alloy and then removing the excess solder by using 'air knives', which blow hot air across the surface of the board. Explore why lead free HASL is a hassle?

One of the unintended benefits of the HASL process is that it will expose the PCB to temperatures up to 265°C which will identify any potential delamination issues well before any expensive components are attached to the board.

Printed Circuit Board with HASL / Lead Free HASL Surface Finish

Advantages:

• Low Cost
• Widely Available
• Re-workable
• Excellent Shelf Life

Disadvantages:

• Uneven Surfaces
• Not Good for Fine Pitch
• Contains Lead (HASL)
• Thermal Shock
• Solder Bridging
• Plugged or Reduced PTH's (Plated Through Holes)

Immersion Tin

According to IPC, the Association Connecting Electronics Industry, Immersion Tin (ISn) is a metallic finish deposited by a chemical displacement reaction that is applied directly over the basis metal of the circuit board, that is, copper. The ISn protects the underlying copper from oxidation over its intended shelf life.

Copper and tin however have a strong affinity for one another. The diffusion of one metal into the other will occur inevitably, directly impacting the shelf life of the deposit and the performance of the finish. The negative effects of tin whiskers growth are well described in industry related literature and topics of several published papers.

Printed Circuit Board with Immersion Tin Surface Finish

Advantages:

• Flat Surface
• No Pb
• Re-workable
• Top Choice for Press Fit Pin Insertion

Disadvantages:

• Easy to Cause Handling Damage
• Process Uses a Carcinogen (Thiourea)
• Exposed Tin on Final Assembly can Corrode
• Tin Whiskers
• Not Good for Multiple Reflow/Assembly Processes
• Difficult to Measure Thickness

Immersion Silver

Immersion silver is a non-electrolytic chemical finish applied by immersing the copper PCB into a tank of silver ions. It is a good choice finish for circuit boards with EMI shieldingand is also used for dome contacts and wire bonding. The average surface thickness of the silver is 5-18 microinches.

With modern environmental concerns such as RoHS and WEE, immersion silver is environmentally better than both HASL and ENIG. It is popular also due to its lesser cost than ENIG.

Printed Circuit Board with Immersion Silver Surface Finish

Advantages:

• Applies more evenly than HASL
• Environmentally better than ENIG and HASL
• Shelf life equal to HASL
• More cost-effective than ENIG

Disadvantages:

• Must be soldered within the day the PCB is removed from storage
• Can be tarnished easily with improper handling
• Less durable than ENIGdue to no layer of nickel underneath

OSP / Entek

OSP (Organic Solderability Preservative) or anti-tarnish preserves the copper surface from oxidation by applying a very thin protective layer of material over the exposed copper usually using a conveyorized process.

It uses a water-based organic compound that selectively bonds to copper and provides an organometallic layer that protects the copper prior to soldering. It's also extremely green environmentally in comparison with the other common lead-free finishes, which suffer from either being more toxic or substantially higher energy consumption. Here is a blog post on when and when not to bake OSP circuit boards before use.

Printed Circuit Board with OSP / Entek Surface Finish

Advantages:

• Flat Surface
• No Pb
• Simple Process
• Re-workable
• Cost Effective

Disadvantages:

• No Way to Measure Thickness
• Not Good for PTH (Plated Through Holes)
• Short Shelf Life
• Can Cause ICT Issues
• Exposed Cu on Final Assembly
• Handling Sensitive

Electroless Nickel Immersion Gold (ENIG)

ENIG is a two layer metallic coating of 2-8 μin Au over 120-240 μin Ni. The Nickel is the barrier to the copper and is the surface to which the components are actually soldered to. The gold protects the nickel during storage and also provides the low contact resistance required for the thin gold deposits. ENIG is now arguably the most used finish in the PCB industry due the growth and implementation of the RoHs regulation. Check out this related post, Proper Handling of ENIG and Immersion PCB Surface Finishes.

Printed Circuit Board with Electroless Nickel Immersion Gold (ENIG) Surface Finish

Advantages:

• Flat Surface
• No Pb
• Good for PTH (Plated Through Holes)
• Long Shelf Life

Disadvantages:

• Expensive
• Not Re-workable
• Black Pad / Black Nickel
• Damage from ET
• Signal Loss (RF)
• Complicated Process

Electroless Nickel Electroless Palladium Immersion Gold (ENEPIG)

ENEPIG, a relative newcomer to the circuit board world of finishes, first came on the market in the late 90s. This three-layer metallic coating of nickel, palladium, and gold provides an option like no others: it is bondable. ENEPIG’s first crack at a printed circuit board surface treatment fizzled with manufacturing due to its extreme high cost layer of palladium and low demand of use.

The need for a separate manufacturing line was not receptive for these same reasons. Recently, ENEPIG has made a comeback as the potential to meet reliability, packaging needs, and RoHS standards are a plus with this finish. It is perfect for high frequency applications where spacing is limited.

When compared to the other top four finishes, ENIG, Lead Free-HASL, immersion silver and OSP, ENEPIG outperforms all on the after-assembly corrosion level. Learn more here, ENEPIG Printed Circuit Boards.

Printed Circuit Board with Electroless Nickel Electroless Palladium Immersion Gold (ENEPIG) Surface Finish

Advantages:

• Extremely Flat Surface
• No Lead Content
• Multi-Cycle Assembly
• Excellent Solder Joints
• Wire Bondable
• No Corrosion Risks
• 12 Month or Greater Shelf Life
• No Black Pad Risk

Disadvantages:

• Still Somewhat More Expensive
• Is Re-Workable with Some Limitations
• Processing Limits

Gold – Hard Gold

Hard Electrolytic Gold consists of a layer of gold plated over a barrier coat of nickel. Hard gold is extremely durable, and is most commonly applied to high-wear areas such as edge connector fingers and keypads.

Unlike ENIG, its thickness can vary by controlling the duration of the plating cycle, although the typical minimum values for fingers are 30 μin gold over 100 μin nickel for Class 1 and Class 2, 50 μin gold over 100 μin nickel for Class 3.

Hard gold is not generally applied to solderable areas, because of its high cost and its relatively poor solderability. The maximum thickness that IPC considers to be solderable is 17.8 μin, so if this type of gold must be used on surfaces to be soldered, the recommended nominal thickness should be about 5-10 μin.

Printed Circuit Board with Gold – Hard Gold Surface Finish

Advantages:

• Hard, Durable Surface
• No Pb
• Long Shelf Life

Disadvantages:

• Very Expensive
• Extra Processing / Labor Intensive
• Use of Resist / Tape
• Plating / Bus Bars required
• Demarcation
• Difficulty with Other Surface Finishes
• Etching Undercut can Lead to Slivering / Flaking
• Not Solderable Above 17 μin
• Finish Does Not Fully Encapsulate Trace Sidewalls, Except in Finger Areas

Conclusion

It is important to select the appropriate surface finish for your project by considering the various options while factoring in performance requirements and material costs.

For an example, if you are looking for the lowest cost then Tin-Lead HASL might seem like a good choice, but it is not suitable for RoHS-compliant products. If your product does require RoHS, you might consider lead-free HASL. That is only if there are no fine pitch components, since LFHASL cannot be applied perfectly flat. If your design needs to be RoHS compliant and does use fine pitch components, then you'll need to select a flat, lead-free finish, such as Immersion Silver or ENIG. Bear in mind that doing so will necessitate the use of more costly high temperature laminate.

Unsure of what you will need? Consult with a PCB fabricator prior to you making a selection. This will ensure that the combination of the surface finish and material will result in a high-yielding, cost-effective design that will perform as expected.

For more information on circuit board surface finishes, check out our blog posts on why you should bake OSP circuit boards before use and proper circuit board handling with immersion finishes.

Not Sure What Surface Finish Is Best For Your Application?

Our team of experienced engineers is here to help you design a custom PCB solution, utilizing the various surface finished from HASL, Immersion Tin, OSP/Entek, ENIG, ENEPIG, or Hard Gold.